Spheroidal graphite cast iron for ultra low temperature

초저온용 구상흑연주철

Abstract

PURPOSE: Spherical graphite cast iron for ultra low temperature is provided to ensure high tensile strength and hardness, thereby satisfying high low-temperature impact property and elongation rate under ultra low temperature that are required for parts of a special ship which sails in polar regions. CONSTITUTION: Spherical graphite cast iron for ultra low temperature comprises carbon 3.37~3.97wt%, manganese 0.100~0.149wt%, phosphorus 0.025~0.033wt%, sulfate 0.001~0.01wt%, chrome 0.01~0.05wt%, magnesium 0.030~0.044wt%, silicon 1.69~2.09wt%, nickel 0.850~0.900wt%, and iron and inevitable impurities of the remaining amount. The spherical graphite cast iron has ferrite-based organizations of 90~100% and a speroidization rate of 90~100%.
본 발명은 탄소 3.37~3.97wt%, 망간 0.100~0.149wt%, 인 0.025~0.033wt%, 황 0.001~0.01wt%, 크롬 0.01~0.05wt%, 마그네슘 0.030~0.044wt%, 규소 1.69~2.09wt%, 니켈 0.850~0.900wt%를 포함하여 이루어지고, 나머지는 철 및 불가피한 불순물을 포함하여 이루어지는 초저온용 구상흑연주철에 관한 것으로서, 높은 인장강도와 경도로 인하여 초저온에서도 높은 기계적 특성인 저온충격특성 및 높은 연신율을 갖아 극지방을 운행하는 특수선박의 부품이 저온에서 파괴되는 것을 방지하는 초저온용 구상흑연주철에 관한 분야이다. 또한 본 발명에 의한 초저온용 구상흑연주철은 높은 인장강도와 경도로 인하여 초저온에서도 높은 기계적 특성인 저온충격특성 및 높은 연신율을 갖아 극지방을 운행하는 특수선박의 부품이 저온에서 쉽게 냉각되어 외부충격에 의해 파괴되는 문제를 해결하는 효과가 있다.

Claims

Description

Topics

Download Full PDF Version (Non-Commercial Use)